DuPont™ Kapton® FWR is a heat fusible polyimide-FEP fluoropolymer composite film that has a unique balance of excellent electrical, thermal durability, and chemical resistance properties. The properties of Kapton® FWR will provide a tough, high dielectric strength insulation with significantly improved hydrolysis resistance compared to other commonly used polyimide materials. Kapton® FWR can be properly processed on most tape wrapping machines. It can be fused using either induction or radiant heat. Kapton® FWR films have a higher modulus and lower water vapor permeability than equivalent Kapton® FN films. The wire wrapping and sealing process may have to be modified to compensate for these differences
Kapton® 150FWR019 film is constructed of a 1.0 mil Kapton® polyimide film with 0.5 mil of FEP fluoropolymer on one side.
|
|
| Gross Weight | Net Weight | Carton Eacht | Carton Length | Carton Weight | Carton Height |
|---|---|---|---|---|---|
| 781 | 0 | 0 | 0 |
| Property | Method | Unit | Value |
|---|---|---|---|
| Thickness (kptn-111) | ASTM D-374 | mil | 1.5 |
| ASTM D-374 | µm | 38 | |
| ASTM D-374 | mil | 2 | |
| ASTM D-374 | µm | 50 | |
| Tensile Strength (kptn-103) | ASTM D-882 | MPa | 234 |
| ASTM D-882 | kpsi | 34 | |
| ASTM D-882 | MPa | 207 | |
| ASTM D-882 | kpsi | 30 | |
| Tensile Modulus (kptn-99) | ASTM D-882 | GPa | 3.6 |
| ASTM D-882 | kpsi | 520 | |
| ASTM D-882 | GPa | 3 | |
| ASTM D-882 | kpsi | 430 | |
| Dielectric Strength (kptn-19) | ASTM D-149 (kptn-5) | kV/mm | 177 |
| ASTM D-149 (kptn-5) | V/mil | 4500 | |
| — (kptn-1) | kV/mil | 5.4 | |
| ASTM D-149 (kptn-5) | kV/mm | 197 | |
| ASTM D-149 (kptn-5) | V/mil | 5000 | |
| — (kptn-1) | kV/mil | 5.6 | |
| Yield | — (kptn-1) | m²/kg | 16.3 |
| — (kptn-1) | ft²/lb | 79.7 | |
| — (kptn-1) | m²/kg | 11.6 | |
| — (kptn-1) | ft²/lb | 56.8 | |
| Elongation (kptn-22) | ASTM D-882 | % | 60 |
| ASTM D-882 | % | 63 | |
| Dielectric Constant | ASTM D-150 (kptn-10) | — | 2.7 |
| ASTM D-150 (kptn-10) | — | 2.7 | |
| Hydroscopic Coefficient of Expansion | — (kptn-1) | ppm/% RH | 9 |
| — (kptn-1) | ppm/% RH | 9 | |
| Moisture Absorption, 100% RH | ASTM D-570 (kptn-31) | % | 2.2 |
| ASTM D-570 (kptn-31) | % | 2.2 | |
| Water Vapor Permeability (kptn-127) | ASTM E-96 | g/m2 /day | 8.4 |
| ASTM E-96 | g/m2 /day | 8.4 | |
| Density (kptn-17) | ASTM D-1505 | g/cc | 1.69 |
| ASTM D-1505 | g/cc | 1.83 | |
| UL Mechanical RTI | UL746B | °C | 200 |
| UL746B | °C | 200 | |
| UL Electrical RTI | UL746B | °C | 240 |
| UL746B | °C | 240 | |
| Dissipation Factor at 1 kHz | ASTM D-150 (kptn-10) | — | 0.0013 |
| ASTM D-150 (kptn-10) | — | 0.0013 | |
| Flammability (kptn-29) | UL Test Method | UL-94 | V-0 |
| UL Test Method | UL-94 | V-0 | |
| Volume Resistivity (kptn-120) | ASTM D-257 (kptn-21) | ohm-cm | 2.3017 |
| ASTM D-257 (kptn-21) | ohm-cm | 2.3017 |
|
Fabric/material |
KAP/TEF LAM FILM |
|---|---|
|
Design |
150FWR019 |
|
Seam |
LAMINATED FILMS |
|
Packaging |
150FWR019 |
|
Hazard |
|
|
Coated Material |
HPF FLM SF&FP |
|
Features |
LAMINATED FILMS |